Non-fuming pickling solution for copper, brass, aluminum and other non-ferrous alloys
※ ACTANE 97
Chemicals
General purpose
Oxide film removal
Various metals
※ ACTANE 97
※This product can only be sold to Japan, Malaysia, Indonesia, Thailand, Philippines, Brunei, Vietnam, Singapore, South Korea, Taiwan, Hong Kong, and China under a license agreement.
ACTANE 97 is a non-fuming pickling solution for copper, brass, aluminum and other non-ferrous alloys.
◆Features
1. Operated at room temperature, ACTANE 97 solution removes heat treat scale and oxides, including red cuprous oxide from copper alloys, and copper smut from aluminum alloys.
2. It is ideal for use prior to electroplating to activating difficult-to-plate alloys, such as beryllium copper, leaded brass, phosphor bronze and tin-lead solders. Combinations of metals, such as soldered assemblies of aluminum and brass, can be activated for plating in ACTANE 97.
3. ACTANE 97 replaces concentrated liquid acid dips such as nitric-sulfuric, nitric-phosphoric and chromic-sulfuric. ACTANE 97 removes oxides and produces a smooth, lustrous surface which will plate bright from subsequent bright plating baths. Although the brightness produced is not as great as that obtained from nitric-sulfuric bright dip, the results after bright nickel plating are the same. The brightness will equal that obtained from a chromic-sulfuric dip.
ACTANE 97 is a non-fuming pickling solution for copper, brass, aluminum and other non-ferrous alloys.
◆Features
1. Operated at room temperature, ACTANE 97 solution removes heat treat scale and oxides, including red cuprous oxide from copper alloys, and copper smut from aluminum alloys.
2. It is ideal for use prior to electroplating to activating difficult-to-plate alloys, such as beryllium copper, leaded brass, phosphor bronze and tin-lead solders. Combinations of metals, such as soldered assemblies of aluminum and brass, can be activated for plating in ACTANE 97.
3. ACTANE 97 replaces concentrated liquid acid dips such as nitric-sulfuric, nitric-phosphoric and chromic-sulfuric. ACTANE 97 removes oxides and produces a smooth, lustrous surface which will plate bright from subsequent bright plating baths. Although the brightness produced is not as great as that obtained from nitric-sulfuric bright dip, the results after bright nickel plating are the same. The brightness will equal that obtained from a chromic-sulfuric dip.